12.7-PO-X-BK | 세부

Application	HUS876 is used where high flame retardany is required. It is very versatile because of its good mechanical and chemical properties, so it is used for insulation, mechanical protection, strain relief and marking.
Behaviour At Low Temperature	not cracking, not breaking
Behaviour at Heat Shock	not cracking, not fluid, not breaking
Behaviour at low Temperature test method	ASTM D2671
Colour	Black (BK)
Elongation At Heat Aging	400%
Heat Aging Test	168h/175°C
Heat Aging test method	ISO 37
Heat Shock Test	4h/250°C
Material	Polyolefin, cross-linked (PO-X)
PART DESCRIPTION	HUS876 25.4/12.7-PO-X-BK
Pack Content	50m
Package Content packed in	metre
Shrink Ratio	2:1
Size	1"
Type	HUS876 25.4/12.7
Variant	Thin-Wall
With inner glue (Yes/No)	No


Longitudinal Change After Shrinkage	+/-5%
Recov. ∅ d max.	12.7mm
Supplied ∅ D min.	25.4mm
Wall (WT)	0.90mm

Dielectric Strength	20kV/mm
Dielectric Strength test method	ASTM D150
ELV compliant (Article 4 - 2)	YES
Elongation at break	400%
Elongation at break test method	ISO 37
Hazardous Goods	No
Insulation Class	B (VDE 0530)
Min. Shrink Temperature - °C	+85 °C
Operating Temperature	-55 °C to +135 °C
ROHS compliant	Yes
Specifications	CSA, MIL-DTL-23053/5C, UL 224 VW-1
Specifications
Tensile Strength	17MPa
Test Method Tensile Strength	ISO 37
UL OCD link	Link
UL Recognized (US and Canada)	Yes
UL-File Number	E143529
Volume Resistance	10¹⁶ Ω cm
Volume Resistance test method	ASTM D2671
Water Absorption	0.5%