Heat shrink marker, thermal transfer print, continuous, 38.1mm/19.1mm, black, 10m
Art.-No. 551-41117 | THTT381BK-PVDFX-BK | Details

This product is not available anymore.

More products in this product group:

Application	THTT is a 2:1 high temperature, flame retardant heat shrink marker supplied in continuous tube and on convenient reels that allows printing on both sides if required. The printed marker is ideal for use in applications where high temperature and exposure to aggressive solutions are found. The tubing has been especially prepared so that the print performance is excellent at all times using HellermannTyton's printer range. A standard heat gun with reflector is used to shrink the sleeves onto the wire or cable to achieve a permanent mark. In addition it is possible to either perforate the tubing at pre-determined lengths or fully sever the markers. The material is also especially formulated to be printable with laser beam printers.
Behaviour at low Temperature test method	ASTM D2671
Colour	Black (BK)
Fixation Method	Suspend
Heat Aging Test	168h/225°C
Heat Aging test method	ASTM D638
Heat Shock Test	4h/275°C
Material	Polyvinylidene Fluoride cross-linked (PVDFX)
PART DESCRIPTION	THTT381BK-PVDFX-BK
Pack Cont.	10m
Package Content packed in	carton
Printable	Yes
Product Family	THTT – 2:1 Aerospace High Temperature
Product Group	Shrinkable markers "Continuous Tube", thermal transfer
Short Description	High temperature shrinkable markers continuous THTT 2:1 printable 38.1/19.1 black 10m/box = 1 reel
Shrink Ratio	2:1
Type	THTT381BK
Variant	Roller form
With inner glue (Yes/No)	No
With label space	Yes


Height (H)	62.0mm
Longitudinal Change After Shrinkage	-10% max.
Longitudinal Change After Shrinkage test method	UL 224
Print Method	thermal transfer print
Print Method (Alternative)	laser beam print
Recov. ∅ d max.	19.1mm
Supplied ∅ D min.	38.1mm
Wall (WT)	0.60mm
Weight/Unit	0.1342kg

ELV compliant (Article 4 - 2)	YES
Elongation at break	300 %
Elongation at break test method	ASTM D638
Hazardous Goods	No
Min. Shrink Temperature - °C	+120 °C
Operating Temperature	-55 °C to +225 °C
ROHS compliant	Yes
Recommended Ribbon Type	TTRHT
Reel Variant	continuous
Specifications
Specifications	MIL-STD-202G Method 215K, SAE - AS81531
Tensile Strength	31MPa
Test Method Tensile Strength	ASTM D638
Volume Resistance	10¹² Ω cm
Volume Resistance test method	ASTM D876
Water Absorption	0.50%