Heat shrinkable tubing up to 3.5:1 - 1 m lengths
Številka proizvoda 321-20851
| HA47-85/25-PO-X-BK
|
Podrobnosti
- Thick wall polyolefin adhesive-lined sleeving
- Thermoplastic adhesive protects against moisture and weathering
- Used for low voltage power applications
![](https://www.hellermanntyton.com/shared/speclogos/99593_All_Languages.jpg)
![](https://www.hellermanntyton.com/shared/speclogos/99595_All_Languages.jpg)
More products in this product group:
Application | The toughness and wheatherability makes it well suited for exposed applications and underground cable joints and cable terminations. |
Application Tool | CHG900 |
Behaviour At Low Temperature | not cracking |
Behaviour at Heat Shock | not cracking, not fluid, not dripping |
Behaviour at low Temperature test method | ASTM D2671 |
Colour | Black (BK) |
Elongation At Heat Aging | 300% |
Heat Aging Test | 168h/150°C |
Heat Aging test method | ASTM D2671 |
Heat Shock Test | 4h/225°C |
Material | Polyolefin, cross-linked (PO-X) |
Minimum Tensile Strength At Heat Aging | 12MPa |
PART DESCRIPTION | HA47-85/25-PO-X-BK |
Pack Cont. | 1.2m |
Package Content packed in | lengths |
Printable | No |
Product Family | HA47 - thick wall adhesive lined |
Product Group | Heat shrinkable tubing up to 3.5:1 - 1 m lengths |
Shrink Ratio | up to 4:1 |
Size | 3-3/8" |
Type | HA47-85/25 |
Variant | Thick-Wall |
With inner glue (Yes/No) | Yes |
Adhesive | Hot melt adhesive |
Dielectric Strength | 15kV/mm |
Dielectric Strength test method | IEC 60243 |
Elongation at break | 350 |
Elongation at break test method | ASTM D2671 |
Halogen-free | Yes |
Insulation Class | A (VDE 0530) |
Min. Shrink Temperature - °C | +120 °C |
Operating Temperature | -55 °C to +110 °C |
ROHS compliant | Yes |
Softening Point Adhesive | +85 °C |
Specifications |
![]() ![]() |
Tensile Strength | 12MPa |
Tensile Strength test method | IEC 93 |
Test Method Tensile Strength | ASTM D2671 |
UL Listed (US and Canada) | No |
UL Recognized (US and Canada) | No |
Volume Resistance | 10¹² Ω cm |
Water Absorption | 0.2% |